ZHUZHOU JIABANG REFRACTORY METAL CO., LTD.
Molybdenum Faced Electrode

Molybdenum Faced Electrode

Send Inquiry

Developed from premium grade BeCu and copper, the offered Molybdenum Faced Electrode is notable for its silver white color. It possesses 2610oC melting point and high electrical conductivity level. Apart from that, this electrode is acknowledged for its low vapor pressure rate and good thermal conductivity level. The offered item has extensive utilization in different industries that include electronics, smelting, chemical processing, machinery and aerospace. As a growth oriented manufacturer, we are offering premium quality Molybdenum Faced Electrode which is accessible in different specifications.
Features

  • It has 2610oC melting point
  • High conductivity
  • It can prevent corrosion caused by glass and molten metal

Technical Specification :

RWMA Group A
CuCr and CuCrZr

Content (%wt.)

Density (g/cm3)

Conductivity (%IACS)

Hardness (HRB)

RWMA

Cr: 0.6-1%

8.9

70

85

Class 2

Cr: 0.5-1.5%, Zr: 0.05-0.25%, Cu: balance

8.9

80

80

Class 2


Nickel Silicon Copper

Composition

Density (g/cm3)

Conductivity (%IACS)

Hardness (HRB)

RWMA

Si: 0.60-1.1% Ni: 2.4-3.4% Cu: balance

8.83

40

90

Class 3


CuCo2Be

Content (%wt.)

Density (g/cm3)

Conductivity (%IACS)

Hardness (HRB)

RWMA

Be: 0.40-0.70% Co: 2.40-2.70% Cu: balance

8.83

45

95

Class 3


RWMA Group B

Refractory Metal
Tungsten copper :

Composition

Density (g/cm3)

Hardness (HRB)

Conductivity (%IACS)

RWMA

W50Cu50

11.9

65

54


W55Cu45

12.5

70

49

Class 10

W70Cu30

14.1

82

42


W75Cu25

14.5

90

38

Class 11

W80Cu20

15.2

98

34

Class 12

W85Cu15

15.9

240HB

30


W90Cu10

16.75

260HB

27



Tungsten

Composite (%wt.)

Density (g/cm3)

Hardness (HRC)

Electrical Conductivity (%IACS)

Class

RWMA

Comparison

W 99.95

19.3

36

30

13

13.743

High temperature resistance

W-Ce (CeO2:2%)

19.2





Low electric discharge power, fine arc-starting performance, excellent arc erosion resistance, longer service life

W-La (La2O3: 1-2%)

19.2





Low electric discharge power, easy for machining


Molybdenum

Comparison (wt.%)

Density (g/cm³)

Hardness (HRB)

Electrical Conductivity (%IACS)

RWMA

Comparison

Mo  99.95

10.2

90 HRB

30

14.423

Superior electrical and thermal conductivity

TZM (Ti: 0.5%, Zr: 0.08%, C: 0.02%)

10.17




High thermal and creep resistance

Mola (La2O3: 0.1 -1.8%)

10.19